- 缺口沖擊強度: 0.534
- 拉伸強度 [MPa]: 138.0
- 彎曲模量 [MPa]: 11.0
- 熱變形溫度 [℃]: 260.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 138 MPa | 20000 psi | ASTM D638 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 - 0.801 J/cm @Temperature 22.8 °C | 1.00 - 1.50 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 - 263 °C | 500 - 505 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 - 257 °C | 490 - 495 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 293 - 316 °C | 560 - 600 °F | |
| Mold Temperature | 93.3 - 121 °C | 200 - 250 °F | |
| Dry Time | <= 4 hour @Temperature 93.3 °C | <= 4 hour @Temperature 200 °F | to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.552 - 0.862 MPa | 80.0 - 125 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 60 - 100 rpm | 60 - 100 rpm | |