- 熔體流動速率 [g/10min]: 42.6
- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 4.0
- 缺口沖擊強度: 9.0
- 拉伸強度 [MPa]: 140.0
- 彎曲模量 [MPa]: 7.40
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in3 | ISO 1183 | ||
| Water Absorption | 4.0 - 4.6 % | 4.0 - 4.6 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.1 - 1.5 % | 1.1 - 1.5 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | restricted | ||
| Melt Flow | 42.6 g/10 min @Load 5.00 kg, Temperature 275 °C | 42.6 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 140 MPa | 20300 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.8 % | 3.8 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 7.40 GPa | 1070 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 160 MPa | 23200 psi | at max force; ISO 178 | ||
| Flexural Modulus | 7.40 GPa | 1070 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 6.00 J/cm2 @Temperature 23.0 °C | 28.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 4.6 @Frequency 1.00 Hz | 4.6 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.10 @Frequency 1.00e+6 Hz | 0.10 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||