- 熔體流動速率 [g/10min]: 31.2
- 密度 [g/cm3]: 1.56
- 吸水率 [%]: 3.7
- 缺口沖擊強度: 14.5
- 拉伸強度 [MPa]: 180.0
- 彎曲模量 [MPa]: 13.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |||
| Density | 1.56 g/cc | 0.0564 lb/in3 | ISO 1183 | ||
| Water Absorption | 3.7 - 4.3 % | 3.7 - 4.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.0 - 1.4 % | 1.0 - 1.4 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | restricted | ||
| Linear Mold Shrinkage, Flow | 0.0033 cm/cm | 0.0033 in/in | ISO 2577 | ||
| 0.0045 cm/cm | 0.0045 in/in | TM=300°C, TW=80°C | |||
| Linear Mold Shrinkage, Transverse | 0.0082 cm/cm | 0.0082 in/in | ISO 2577 | ||
| Melt Flow | 31.2 g/10 min @Load 5.00 kg, Temperature 275 °C | 31.2 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 180 MPa | 26100 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 12.5 GPa | 1810 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 300 MPa | 43500 psi | at max force; ISO 178 | ||
| Flexural Modulus | 13.5 GPa | 1960 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 14.5 kJ/m2 @Temperature 23.0 °C | 6.90 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 10.0 J/cm2 @Temperature 23.0 °C | 47.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 2.50 J/cm2 @Temperature 23.0 °C | 11.9 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 7800 MPa @Strain <=0.500 % | 1.13e+6 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 6.6 @Frequency 1.00 Hz | 6.6 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.17 @Frequency 1.00e+6 Hz | 0.17 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |||
| Thermal Conductivity | 0.370 W/m-K | 2.57 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 165 °C | 329 °F | for 50% loss of tensile strength after 5000hr | |||
| 240 °C | 464 °F | ||||
| Decomposition Temperature | >= 310 °C | >= 590 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | Injection-molding/Extrusion | ||
| 300 °C | 572 °F | Optimal | |||
| Mold Temperature | 80.0 °C | 176 °F | Optimal | ||
| 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D129 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||