- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 6.4
- 缺口沖擊強度: 0.85
- 彎曲強度 [MPa]: 180.0
- 彎曲模量 [MPa]: 7.59
- 熱變形溫度 [℃]: 262.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in3 | ISO 1183 | ||
| Water Absorption | 6.4 % | 6.4 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 172 MPa | 24900 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 180 MPa | 26100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 8.80 GPa | 1280 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 260 MPa | 37700 psi | ASTM Test | ||
| Flexural Modulus | 7.59 GPa | 1100 ksi | ASTM Test | ||
| 8.00 GPa | 1160 ksi | ISO Data | |||
| Izod Impact, Notched | 0.850 J/cm @Thickness 3.17 mm | 1.59 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | ISO Test | ||
| Charpy Impact Unnotched | 7.00 J/cm2 | 33.3 ft-lb/in2 | ISO 179 | ||
| 5.50 J/cm2 @Temperature -30.0 °C | 26.2 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.00 J/cm2 | 4.76 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | ISO 75 | ||
| 297 °C | 567 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM Test | ||
| 250 °C | 482 °F | ISO 75 | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||