- 吸水率 [%]: 2.3
- 彎曲模量 [MPa]: 5.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 20 % | 20 % | ISO 1172 |
| Water Absorption | 2.3 - 2.5 % @Temperature 23.0 °C | 2.3 - 2.5 % @Temperature 73.4 °F | 50% r.h.; ISO 62 |
| Water Absorption at Saturation | 6.7 - 7.2 % @Time 82800 sec | 6.7 - 7.2 % @Time 23.0 hour | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 [mm/min]; ISO 527-1/2 |
| 50.0 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec | 7250 psi @Temperature 320 - 347 °F, Time 5000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |
| 50.0 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec | 7250 psi @Temperature 266 - 302 °F, Time 20000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |
| Elongation at Break | 8.0 % | 8.0 % | 5 [mm/min]; ISO 527-1/2 |
| Tensile Modulus | 4.60 GPa | 667 ksi | 1[mm/min]; ISO 527-1/2 |
| Flexural Strength | 165 MPa | 23900 psi | 2 [mm/min]; ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | 2 [mm/min]; ISO 178 |
| Charpy Impact Unnotched | 8.60 J/cm2 @Temperature 23.0 °C | 40.9 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 1.10 J/cm2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | ISO 11357-1/3 |