- 密度 [g/cm3]: 1.22
- 缺口沖擊強度: 0.9
- 彎曲強度 [MPa]: 117.0
- 彎曲模量 [MPa]: 6.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 117 MPa @Thickness 3.17 mm | 17000 psi @Thickness 0.125 in | ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.17 mm | 3.0 % @Thickness 0.125 in | ASTM D638 |
| Flexural Modulus | 6.80 GPa @Thickness 3.17 mm | 986 ksi @Thickness 0.125 in | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm @Thickness 3.17 mm | 1.69 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | |