- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 9.5
- 熱變形溫度 [℃]: 290.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in3 | ISO 1183 | ||
| Water Absorption | 9.5 % | 9.5 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 3.1 % | 3.1 % | Humidity Absorption; Sim. to ISO 62 | ||
| Viscosity Test | 150 cm3/g | 150 cm3/g | Viscosity Number | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527-1/-2 | ||
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 6.10 GPa | 885 ksi | ISO 527-1/-2 | ||
| Charpy Impact, Notched | 0.450 J/cm2 @Temperature 23.0 °C | 2.14 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 μm/m-°C @Temperature 20.0 °C | 16.7 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C @Temperature 20.0 °C | 50.0 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 290 °C | 554 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 290 °C | 554 °F | 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | Glass Transition Temperature (10°C/min); ISO 11357-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Platable | Yes | ||||
| With Fillers | Yes | ||||