- 密度 [g/cm3]: 1.56
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 |
| Tensile Modulus | 9.20 GPa | 1330 ksi | ISO 527-1/-2 |
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 μm/m-°C @Temperature 20.0 °C | 16.7 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C @Temperature 20.0 °C | 44.4 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 |