- 密度 [g/cm3]: 1.1
- 拉伸強度 [MPa]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 50% RH / 23°C; Similar to ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
| Elongation at Yield | >= 50 % | >= 50 % | Nominal Strain at Yield; ISO 527-1/-2 |
| Tensile Modulus | 1.85 GPa | 268 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 7.50 J/cm2 | 35.7 ft-lb/in2 | ISO 179/1eU |
| 2.60 J/cm2 @Temperature -30.0 °C | 12.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 475 V | 475 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 160 μm/m-°C @Temperature 20.0 °C | 88.9 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 180 μm/m-°C @Temperature 20.0 °C | 100 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75-1/-2 |