- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.9
- 缺口沖擊強度: 0.641
- 拉伸強度 [MPa]: 82.7
- 斷裂伸長率 [%]: 110
- 彎曲強度 [MPa]: 110.0
- 彎曲模量 [MPa]: 2.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 - 1.69 g/cc | 0.0517 - 0.0611 lb/in?? | Average value: 1.53 g/cc Grade Count:13 |
| Water Absorption | 0.900 - 2.00 % | 0.900 - 2.00 % | Average value: 1.59 % Grade Count:8 |
| Linear Mold Shrinkage | 0.00200 - 0.00750 cm/cm | 0.00200 - 0.00750 in/in | Average value: 0.00533 cm/cm Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 110 - 205 MPa | 16000 - 29700 psi | Average value: 159 MPa Grade Count:7 |
| Tensile Strength, Yield | 82.7 - 179 MPa | 12000 - 26000 psi | Average value: 138 MPa Grade Count:6 |
| Elongation at Break | 2.70 - 7.00 % | 2.70 - 7.00 % | Average value: 4.30 % Grade Count:10 |
| Elongation at Yield | 2.00 - 3.00 % | 2.00 - 3.00 % | Average value: 2.62 % Grade Count:3 |
| Modulus of Elasticity | 4.10 - 11.0 GPa | 595 - 1600 ksi | Average value: 8.69 GPa Grade Count:7 |
| Flexural Yield Strength | 110 - 279 MPa | 16000 - 40500 psi | Average value: 207 MPa Grade Count:9 |
| Flexural Modulus | 2.96 - 9.65 GPa | 430 - 1400 ksi | Average value: 7.58 GPa Grade Count:11 |
| Izod Impact, Notched | 0.641 - 1.92 J/cm | 1.20 - 3.60 ft-lb/in | Average value: 1.15 J/cm Grade Count:7 |
| Izod Impact, Notched (ISO) | 8.00 - 8.00 kJ/m?? @Temperature -40.0 - -40.0 ??C | 3.81 - 3.81 ft-lb/in?? @Temperature -40.0 - -40.0 ??F | Average value: 8.00 kJ/m?? Grade Count:2 |
| Charpy Impact, Notched | 0.700 - 1.50 J/cm?? | 3.33 - 7.14 ft-lb/in?? | Average value: 1.15 J/cm?? Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+7 - 1.00e+14 ohm-cm | 1.00e+7 - 1.00e+14 ohm-cm | Average value: 4.32e+13 ohm-cm Grade Count:7 |
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | Average value: 23.6 kV/mm Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 - 79.2 ??m/m-??C | 10.0 - 44.0 ??in/in-??F | Average value: 33.0 ??m/m-??C Grade Count:7 |
| Melting Point | 295 ??C | 563 ??F | Average value: 295 ??C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 274 - 290 ??C | 525 - 554 ??F | Average value: 284 ??C Grade Count:10 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 293 - 321 ??C | 560 - 610 ??F | Average value: 309 ??C Grade Count:3 |
| Mold Temperature | 79.4 - 149 ??C | 175 - 300 ??F | Average value: 125 ??C Grade Count:3 |