- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 1.5
- 缺口沖擊強度: 1.07
- 拉伸強度 [MPa]: 55.8
- 彎曲模量 [MPa]: 1.86
- 硬度: 110.0
- 熱變形溫度 [℃]: 174.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | ASTM D792 |
| Water Absorption | 1.5 % @Time 86400 sec | 1.5 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 3.17 mm | 0.013 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 55.8 MPa | 8100 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm, Temperature -40.0 °C | 2.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D256 |
| 2.14 J/cm @Thickness 3.17 mm, Temperature -20.0 °C | 4.00 ft-lb/in @Thickness 0.125 in, Temperature -4.00 °F | ASTM D256 | |
| 3.74 J/cm @Thickness 3.17 mm, Temperature 22.8 °C | 7.00 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ASTM D256 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 95.4 μm/m-°C | 53.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |