- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 1.5
- 缺口沖擊強度: 3.74
- 拉伸強度 [MPa]: 55.2
- 斷裂伸長率 [%]: 82.7
- 彎曲模量 [MPa]: 1.72
- 硬度: 119.0
- 熱變形溫度 [℃]: 174.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | ASTM D792 |
| Water Absorption | 1.5 % @Time 86400 sec | 1.5 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 3.17 mm | 0.013 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 3.74 J/cm @Thickness 3.17 mm | 7.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 95.4 μm/m-°C | 53.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |