- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 5.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | ISO 1183 | ||
| Water Absorption | 5.0 % | 5.0 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 80.0 MPa | 11600 psi | conditioned; ISO 2039-1 | ||
| 135 MPa | 19600 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | conditioned; ISO 527-1/-2 | ||
| 110 MPa | 16000 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 4.0 % | 4.0 % | dry; ISO 527-1/-2 | ||
| 10 % | 10 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 2.10 GPa | 305 ksi | conditioned; ISO 527-1/-2 | ||
| 5.40 GPa | 783 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 4.00 J/cm2 | 19.0 ft-lb/in2 | dry; ISO 179/1eU | ||
| 7.00 J/cm2 | 33.3 ft-lb/in2 | conditioned; ISO 179/1eU | |||
| 3.50 J/cm2 @Temperature 30.0 °C | 16.7 ft-lb/in2 @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 3.50 J/cm2 @Temperature 30.0 °C | 16.7 ft-lb/in2 @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | dry; ISO 179/1eA | ||
| 1.00 J/cm2 | 4.76 ft-lb/in2 | conditioned; ISO 179/1eA | |||
| 0.300 J/cm2 @Temperature 30.0 °C | 1.43 ft-lb/in2 @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.400 J/cm2 @Temperature 30.0 °C | 1.90 ft-lb/in2 @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 100 - 120 °C | 212 - 248 °F | long term; EMS | ||
| 200 °C | 392 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Interior | ||||
| Electricals & Electronics | Electrical appliances | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Housewares | ||||
| Mechanical Engineering | |||||
| Sports & Leisure | |||||
| Tools & Accessories | |||||
| Processing | Injection Molding | ||||