- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 1.3
- 彎曲模量 [MPa]: 4.90
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ISO 1183 |
| Water Absorption | 1.3 - 2.3 % | 1.3 - 2.3 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 6.0 % | 5.0 - 6.0 % | ISO 62 |
| Viscosity Measurement | 155 | 155 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0060 - 0.014 cm/cm | 0.0060 - 0.014 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 155 MPa | 22500 psi | ISO 2039-1 |
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 6.20 GPa | 899 ksi | ISO 527 |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 4.90 GPa | 711 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm2 | 21.4 ft-lb/in2 | DIN 53453 |
| 3.50 J/cm2 @Temperature -40.0 °C | 16.7 ft-lb/in2 @Temperature -40.0 °F | DIN 53453 | |
| Charpy Impact, Notched | 0.900 J/cm2 | 4.28 ft-lb/in2 | DIN 53453 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 242 °C | 468 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 |