- 密度 [g/cm3]: 2.12
- 彎曲強度 [MPa]: 21.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.12 g/cc | 0.0766 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in3 | ASTM D4894 |
| Linear Mold Shrinkage | 0.024 cm/cm | 0.024 in/in | Radial shrinkage of 10 cm o.d. sintered rod at 23°C |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | |
| Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 220 % | 220 % | ASTM D638 |
| Coefficient of Friction, Dynamic | 0.060 | 0.060 | ASTM D1894 |
| Coefficient of Friction, Static | 0.080 | 0.080 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 140 μm/m-°C @Temperature 23.0 - 250 °C | 77.8 μin/in-°F @Temperature 73.4 - 482 °F | ASTM D696 |
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft2-°F | ASTM C177 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous Service |