| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.91 g/cc | 1.91 g/cc | ASTM D792 |
| Water Absorption | 0.1 % | 0.1 % | Immersion, 24hr; ASTM D570(2) |
| Water Absorption at Saturation | 0.3 % | 0.3 % | Immersion; ASTM D570(2) |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Hardness, Shore D | 74 | 74 | ASTM D2240 |
| Tensile Strength | 8.96 MPa | 1300 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.55 GPa | 370 ksi | ASTM D638 |
| Flexural Yield Strength | 17.2 MPa | 2500 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Compressive Strength | 48.3 MPa | 7000 psi | 10% Def.; ASTM D695 |
| Compressive Modulus | 1.38 GPa | 200 ksi | ASTM D695 |
| Shear Strength | 11.7 MPa | 1700 psi | ASTM D732 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | ASTM D256 Type A |
| Coefficient of Friction, Dynamic | <= 0.15 | <= 0.15 | Dry vs. Steel; 20 fpm/250 psi; QTM55007 |
| Coefficient of Friction, Static | <= 0.20 | <= 0.20 | 50 lb load, 90° rotation; QTM55007 |
| K (wear) Factor | 64.5 x 10-8 mm3/N-M | 32.0 x 10-10 in3-min/ft-lb-hr | QTM 55010 |
| Limiting Pressure Velocity | 0.501 MPa-m/sec | 14300 psi-ft/min | 4:1 safety factor; QTM 55007 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | <= 100000 ohm | <= 100000 ohm | EOS/ESD S11.11 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 45.0 μm/m-°C @Temperature -40.0 - 149 °C | 25.0 μin/in-°F @Temperature -40.0 - 300 °F | ASTM E831 |
| Melting Point | 327 °C | 621 °F | Crystalline, Peak; ASTM D3418 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Long Term |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/8 inch (Estimated Rating) |
| Chemical Resistance Properties | Metric | English | Comments |
| Acids, Strong (pH 1-3) | Acceptable | Acceptable | |
| Acids, Weak | Acceptable | Acceptable | |
| Alcohols | Acceptable | Acceptable | |
| Alkalies, Strong (pH 11-14) | Unacceptable | Unacceptable | |
| Alkalies, Weak | Acceptable | Acceptable | |
| Chlorinated Solvents | Acceptable | Acceptable | |
| Conductive / Static Dissipative | Yes | Yes | |
| Continuous Sunlight | Acceptable | Acceptable | |
| Ethers | Acceptable | Acceptable | |
| Hydrocarbons - Aliphatic | Acceptable | Acceptable | |
| Hydrocarbons - Aromatic | Acceptable | Acceptable | |
| Inorganic Salt Solutions | Acceptable | Acceptable | |
| Ketones, Esters | Acceptable | Acceptable | |