- 熔體流動速率 [g/10min]: 2.0
- 缺口沖擊強度: 8.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.77 - 1.78 g/cc | 1.77 - 1.78 g/cc | ISO R1183D |
| Grain Size | <= 30 μm | <= 30 μm | Average size before sieving |
| Melt Flow | 2.0 - 6.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 2.0 - 6.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ISO 868 |
| Tensile Strength at Break | >= 26.0 MPa @Strain >=100 % | >= 3770 psi @Strain >=100 % | ISO R527 |
| Elongation at Break | >= 100 % | >= 100 % | ISO R527 |
| Flexural Strength | 680 MPa | 98600 psi | ISO 178 |
| Izod Impact, Notched | 8.00 J/cm | 15.0 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 141 - 144 °C | 286 - 291 °F | ISO 416C |
| Heat Distortion Temperature | 48.0 °C | 118 °F | ISO 75 |
| Oxygen Index | 43 % | 43 % | Limiting; ASTM D2863 |