- 熔體流動速率 [g/10min]: 2.8
- 彎曲強度 [MPa]: 31.0
- 彎曲模量 [MPa]: 0.586
- 熱變形溫度 [℃]: 77.0
- 透光率 [%]: 96.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.14 g/cc | 2.14 g/cc | ASTM D762 | ||
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 | ||
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ASTM D2116 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 56 | 56 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D1708 | ||
| Elongation at Break | 345 % | 345 % | ASTM D1708 | ||
| Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 | ||
| Compressive Yield Strength | 15.2 MPa @Strain 5.00 % | 2200 psi @Strain 5.00 % | ASTM D695 | ||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| NB @Temperature -60.0 °C | NB @Temperature -76.0 °F | ASTM D256 | |||
| Coefficient of Friction | 0.080 - 0.30 | 0.080 - 0.30 | ASTM D1894 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ASTM D257 | ||
| Dielectric Constant | 2.04 @Frequency 1.30e+10 Hz | 2.04 @Frequency 1.30e+10 Hz | ASTM D1531 | ||
| 2.06 @Frequency 1e+6 Hz | 2.06 @Frequency 1e+6 Hz | ASTM D1531 | |||
| Dielectric Strength | 78.7402 kV/mm | 2000.00 kV/in | 10 mil film; ASTM D149 | ||
| 20.5 kV/mm @Thickness 3.18 mm | 521 kV/in @Thickness 0.125 in | ASTM D149 | |||
| Dissipation Factor | 0.000060 @Frequency 1000 Hz | 0.000060 @Frequency 1000 Hz | ASTM D1531 | ||
| 0.00030 @Frequency 100000 Hz | 0.00030 @Frequency 100000 Hz | ASTM D1531 | |||
| 0.00060 @Frequency 1e+6 Hz | 0.00060 @Frequency 1e+6 Hz | ASTM D1531 | |||
| 0.00070 @Frequency 1.30e+10 Hz | 0.00070 @Frequency 1.30e+10 Hz | ASTM D1531 | |||
| 0.0011 @Frequency 1.00e+9 Hz | 0.0011 @Frequency 1.00e+9 Hz | ASTM D1531 | |||
| Arc Resistance | >= 300 sec | >= 300 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 9.80 J/g | 4.22 BTU/lb | DSC; ASTM D3417 | ||
| CTE, linear | 139 μm/m-°C @Temperature 0.000 - 100 °C | 77.2 μin/in-°F @Temperature 32.0 - 212 °F | ASTM E831 | ||
| 212 μm/m-°C @Temperature 100 - 150 °C | 118 μin/in-°F @Temperature 212 - 302 °F | ASTM E831 | |||
| 270 μm/m-°C @Temperature 150 - 200 °C | 150 μin/in-°F @Temperature 302 - 392 °F | ASTM E831 | |||
| Specific Heat Capacity | 0.242 J/g-°C @Temperature 25.0 °C | 0.0578 BTU/lb-°F @Temperature 77.0 °F | DSC | ||
| 0.267 J/g-°C @Temperature 100 °C | 0.0638 BTU/lb-°F @Temperature 212 °F | DSC | |||
| 0.290 J/g-°C @Temperature 150 °C | 0.0693 BTU/lb-°F @Temperature 302 °F | DSC | |||
| Melting Point | 266 °C | 511 °F | ASTM DTA-E168 | ||
| Maximum Service Temperature, Air | 204 °C | 399 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 °C | 171 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | ASTM D648 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 95 % | >= 95 % | Limiting Oxygen Index; ASTM D2863 | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.341 - 1.347 | 1.341 - 1.347 | |||
| Transmission, Visible | 96 % | 96 % | thin film; solar transmission | ||
| IR Transmittance | 95 % | 95 % | thin film; 0.70 to 3.5 μm | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 360 - 385 °C | 680 - 725 °F | Cure Temperature | ||
| Descriptive Properties | |||||
| 20% Hydrochloric Acid Transmission, g/100sq in. | <0.02 | ||||
| 50% Sodium Hydroxide Transmission, g/100sq in. | <.02 | ||||
| Acetic Acid Transmission, g/100sq in. | 0.41 | ||||
| Acetone Transmission, g/100sq in. | 0.95 | ||||
| Acetophenone Transmission, g/100sq in. | 0.5 | ||||
| Benzene Transmission, g/100sq in. | 0.64 | ||||
| Carbon Tetrachloride Transmission, g/100sq in. | 0.31 | ||||
| Chemical/Solvent Resistance | Excellent | ||||
| Detergent Resist. on grit-blasted aluminum, Hours | 600 | ||||
| Detergent Resistance on aluminum, Hours | 744 | ||||
| Detergent Resistance on grit-blasted steel, Hours | 480 | ||||
| Ethyl Acetate Transmission, g/100sq in. | 0.76 | ||||
| Folding Endurance, # cycles, .18-.20 mm | 5-80 E3 | ||||
| Heat of Combustion J/g | 5100 | ASTM D240 | |||
| Hexane Transmission, g/100sq in. | 0.56 | ||||
| Piperidine Transmission, g/100sq in. | 0.04 | ||||
| Red Fuming Nitric Acid Transmission, g/100sq in. | 7.5-1.4 | ||||
| Salt Spray Resistance on aluminum, Hours | >744 | ||||
| Sulfuric Acid Transmission, g/100sq in. | 0.00001 | ||||
| Water Transmission, g/100sq in. | 0.4 | ||||
| Weather Resistance | 20 | Years unaffected in Florida Exposure | |||