- 熔體流動速率 [g/10min]: 1.7
- 拉伸強度 [MPa]: 14.0
- 彎曲強度 [MPa]: 28.0
- 彎曲模量 [MPa]: 0.600
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.12 - 2.17 g/cc | 2.12 - 2.17 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.050 % | <= 0.050 % | 24 hours; ASTM D570 | ||
| Melt Flow | 1.7 - 3.0 g/10 min | 1.7 - 3.0 g/10 min | ASTM D3307 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 55 | 55 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D3307 | ||
| 15.0 MPa @Temperature 200 °C | 2180 psi @Temperature 392 °F | ASTM D3307 | |||
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D3307 | ||
| Elongation at Break | 260 % | 260 % | ASTM D3307 | ||
| 450 % @Temperature 200 °C | 450 % @Temperature 392 °F | ASTM D3307 | |||
| Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 | ||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | >= 1.00e+17 ohm | >= 1.00e+17 ohm | ASTM D257 | ||
| Dielectric Constant | 2.02 - 2.08 @Frequency 100 - 1.00e+7 Hz | 2.02 - 2.08 @Frequency 100 - 1.00e+7 Hz | ASTM D150 | ||
| Dielectric Strength | 80.0 kV/mm @Thickness 0.0250 mm | 2030 kV/in @Thickness 0.000984 in | film; ASTM D149 | ||
| Dissipation Factor | <= 0.00030 @Frequency 100 - 1.00e+7 Hz | <= 0.00030 @Frequency 100 - 1.00e+7 Hz | ASTM D150 | ||
| Arc Resistance | >= 180 sec | >= 180 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 150 μm/m-°C @Temperature 21.0 - 100 °C | 83.3 μin/in-°F @Temperature 69.8 - 212 °F | ASTM D696 | ||
| 230 μm/m-°C @Temperature 100 - 149 °C | 128 μin/in-°F @Temperature 212 - 300 °F | ASTM D696 | |||
| 290 μm/m-°C @Temperature 149 - 208 °C | 161 μin/in-°F @Temperature 300 - 406 °F | ASTMD 696 | |||
| Melting Point | 285 - 300 °C | 545 - 572 °F | ASTM D3418 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 95 % | >= 95 % | Limiting Oxygen Index; ASTM D2863 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 379 - 399 °C | 714 - 750 °F | Cure Temperature | ||
| Descriptive Properties | |||||
| 20% Hydrochloric Acid Transmission, g/100sq in. | <0.02 | ||||
| 50% Sodium Hydroxide Transmission, g/100sq in. | <.02 | ||||
| Acetic Acid Transmission, g/100sq in. | 0.41 | ||||
| Acetone Transmission, g/100sq in. | 0.95 | ||||
| Acetophenone Transmission, g/100sq in. | 0.5 | ||||
| Benzene Transmission, g/100sq in. | 0.64 | ||||
| Carbon Tetrachloride Transmission, g/100sq in. | 0.31 | ||||
| Chemical/Solvent Resistance | Excellent | ||||
| Ethyl Acetate Transmission, g/100sq in. | 0.76 | ||||
| Heat of Combustion J/g | 5300 | ASTM D240 | |||
| Hexane Transmission, g/100sq in. | 0.56 | ||||
| Piperidine Transmission, g/100sq in. | 0.04 | ||||
| Red Fuming Nitric Acid Transmission, g/100sq in. | 7.5-1.4 | ||||
| Salt Spray Resistance on aluminum, Hours | 1000 | ||||
| Sulfuric Acid Transmission, g/100sq in. | 0.00001 | ||||
| Water Transmission, g/100sq in. | 0.4 | ||||
| Weather Resistance | 10 | Years unaffected in Florida Exposure | |||