- 熔體流動(dòng)速率 [g/10min]: 2.0
- 拉伸強(qiáng)度 [MPa]: 15.2
- 彎曲強(qiáng)度 [MPa]: 28.0
- 彎曲模量 [MPa]: 0.625
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.12 - 2.17 g/cc | 2.12 - 2.17 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.030 % | <= 0.030 % | 24 hours; ASTM D570 | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D3307 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 55 | 55 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D3307 | ||
| 14.0 MPa @Temperature 250 °C | 2030 psi @Temperature 482 °F | ASTM D3307 | |||
| 129 MPa @Temperature -196 °C | 18700 psi @Temperature -321 °F | ASTM D1780 | |||
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | ASTM D3307 | ||
| Elongation at Break | 300 % | 300 % | ASTM D3307 | ||
| 8.0 % @Temperature -196 °C | 8.0 % @Temperature -321 °F | ASTM D1708 | |||
| 500 % @Temperature 250 °C | 500 % @Temperature 482 °F | ASTM D3307 | |||
| Flexural Modulus | 0.625 GPa | 90.6 ksi | ASTM D790 | ||
| 0.0690 GPa @Temperature 250 °C | 10.0 ksi @Temperature 482 °F | ASTM D790 | |||
| Compressive Strength | 24.0 MPa @Temperature 23.0 °C | 3480 psi @Temperature 73.4 °F | ASTM D695 | ||
| 414 MPa @Temperature -196 °C | 60000 psi @Temperature -321 °F | ASTM D695 | |||
| Compressive Modulus | 69.0 GPa @Temperature 23.0 °C | 10000 ksi @Temperature 73.4 °F | ASTM D695 | ||
| 4690 GPa @Temperature -196 °C | 680000 ksi @Temperature -321 °F | ASTM D695 | |||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| 0.640 J/cm @Temperature -196 °C | 1.20 ft-lb/in @Temperature -321 °F | ASTM D256-72a | |||
| Coefficient of Friction, Dynamic | 0.21 | 0.21 | 3 ft/min; 100 psi; dry vs. steel | ||
| 0.214 | 0.214 | 10 ft/min; 100 psi; dry vs. steel | |||
| 0.229 | 0.229 | 30 ft/min; 100 psi; dry vs. steel | |||
| 0.289 | 0.289 | 50 ft/min; 100 psi; dry vs. steel | |||
| K (wear) Factor | 1400 x 10-8 mm3/N-M | 694 x 10-10 in3-min/ft-lb-hr | 50 ft/min; 100 psi; dry vs. steel | ||
| 1980 x 10-8 mm3/N-M | 983 x 10-10 in3-min/ft-lb-hr | 30 ft/min; 100 psi; dry vs. steel | |||
| 3205 x 10-8 mm3/N-M | 1591 x 10-10 in3-min/ft-lb-hr | 3 ft/min; 100 psi; dry vs. steel | |||
| 3700 x 10-8 mm3/N-M | 1837 x 10-10 in3-min/ft-lb-hr | 10 ft/min; 100 psi; dry vs. steel | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | >= 1.00e+17 ohm | >= 1.00e+17 ohm | ASTM D257 | ||
| Dielectric Constant | 2.03 @Frequency 60.0 - 1.00e+6 Hz | 2.03 @Frequency 60.0 - 1.00e+6 Hz | ASTM D150 | ||
| Dielectric Strength | 80.0 kV/mm @Thickness 0.0250 mm | 2030 kV/in @Thickness 0.000984 in | Short time; ASTM D149 | ||
| Dissipation Factor | 0.00010 @Frequency 60.0 - 1.00e+6 Hz | 0.00010 @Frequency 60.0 - 1.00e+6 Hz | ASTM D150 | ||
| Arc Resistance | >= 180 sec | >= 180 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 140 μm/m-°C @Temperature 21.0 - 100 °C | 77.8 μin/in-°F @Temperature 69.8 - 212 °F | ASTM D696 | ||
| 180 μm/m-°C @Temperature 100 - 149 °C | 100 μin/in-°F @Temperature 212 - 300 °F | ASTM D696 | |||
| 220 μm/m-°C @Temperature 149 - 208 °C | 122 μin/in-°F @Temperature 300 - 406 °F | ASTMD 696 | |||
| Specific Heat Capacity | 1.172 J/g-°C @Temperature 100 °C | 0.2801 BTU/lb-°F @Temperature 212 °F | |||
| Melting Point | 302 - 310 °C | 576 - 590 °F | ASTM D3418 | ||
| Maximum Service Temperature, Air | 260 °C | 500 °F | |||
| Glass Transition Temp, Tg | -80.0 °C | -112 °F | Glass II | ||
| 90.0 °C | 194 °F | Glass I | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 95 % | >= 95 % | Limiting Oxygen Index; ASTM D2863 | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.35 | 1.35 | ASTM D542-50 | ||
| Haze | 4.0 % | 4.0 % | ASTM D1003-52 | ||
| Transmission, Visible | 91 - 96 % @Thickness 0.0250 mm | 91 - 96 % @Thickness 0.000984 in | 0.40 to 0.70 μm | ||
| IR Transmittance | 96 - 98 % | 96 - 98 % | 0.025; 0.70 to 2.40 μm | ||
| UV Transmittance | 77 - 91 % @Thickness 0.0250 mm | 77 - 91 % @Thickness 0.000984 in | 0.25 to 0.70 μm | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 379 - 399 °C | 714 - 750 °F | Cure Temperature | ||
| Descriptive Properties | |||||
| 20% Hydrochloric Acid Transmission, g/100sq in. | <0.02 | ||||
| 50% Sodium Hydroxide Transmission, g/100sq in. | <.02 | ||||
| Acetic Acid Transmission, g/100sq in. | 0.41 | ||||
| Acetone Transmission, g/100sq in. | 0.95 | ||||
| Acetophenone Transmission, g/100sq in. | 0.5 | ||||
| Benzene Transmission, g/100sq in. | 0.64 | ||||
| Carbon Tetrachloride Transmission, g/100sq in. | 0.31 | ||||
| Chemical/Solvent Resistance | Excellent | ||||
| Ethyl Acetate Transmission, g/100sq in. | 0.76 | ||||
| Folding Endurance, # cycles, .18-.20 mm | 500000 | ||||
| Heat of Combustion J/g | 5300 | ASTM D240 | |||
| Hexane Transmission, g/100sq in. | 0.56 | ||||
| Piperidine Transmission, g/100sq in. | 0.04 | ||||
| Red Fuming Nitric Acid Transmission, g/100sq in. | 7.5-1.4 | ||||
| Salt Spray Resistance on aluminum, Hours | 1000 | ||||
| Sulfuric Acid Transmission, g/100sq in. | 0.00001 | ||||
| Water Transmission, g/100sq in. | 0.4 | ||||
| Weather Resistance | 10 | Years unaffected in Florida Exposure | |||