- 熔體流動速率 [g/10min]: 3.0
- 彎曲強度 [MPa]: 12.0
- 彎曲模量 [MPa]: 0.590
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.12 - 2.17 g/cc | 2.12 - 2.17 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.030 % | <= 0.030 % | ASTM D570 | ||
| Melt Flow | 3.0 - 7.0 g/10 min | 3.0 - 7.0 g/10 min | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 60 | 60 | ASTM D1706 | ||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 | ||
| Tensile Strength, Ultimate | 12.0 MPa @Temperature 250 °C | 1740 psi @Temperature 482 °F | ASTM D638 | ||
| Elongation at Break | 390 % | 390 % | ASTM D638 | ||
| 680 % @Temperature 250 °C | 680 % @Temperature 482 °F | ASTM D638 | |||
| Flexural Modulus | 0.590 GPa | 85.6 ksi | ASTM D790 | ||
| Izod Impact, Notched | NB | NB | ASTM D256A | ||
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | ASTM D257 | ||
| Dielectric Constant | <= 2.1 @Frequency 60 Hz | <= 2.1 @Frequency 60 Hz | ASTM D150 | ||
| <= 2.1 @Frequency 1000 Hz | <= 2.1 @Frequency 1000 Hz | ASTM D150 | |||
| <= 2.1 @Frequency 1e+6 Hz | <= 2.1 @Frequency 1e+6 Hz | ASTM D150 | |||
| Dissipation Factor | <= 0.00020 @Frequency 60 Hz | <= 0.00020 @Frequency 60 Hz | ASTM D150 | ||
| <= 0.00020 @Frequency 1000 Hz | <= 0.00020 @Frequency 1000 Hz | ASTM D150 | |||
| <= 0.00020 @Frequency 1e+6 Hz | <= 0.00020 @Frequency 1e+6 Hz | ASTM D150 | |||
| Arc Resistance | >= 300 sec | >= 300 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 130 μm/m-°C @Temperature 20.0 °C | 72.2 μin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Specific Heat Capacity | 1.046 J/g-°C | 0.2500 BTU/lb-°F | |||
| Thermal Conductivity | 0.251 W/m-K | 1.74 BTU-in/hr-ft2-°F | ASTM C177 | ||
| Melting Point | 305 - 315 °C | 581 - 599 °F | |||
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 95 % | >= 95 % | ASTM D2863 | ||
| Descriptive Properties | |||||
| Ball Pressure Temperature, °C | 230 | ||||
| Flex Life, Cycles | 200000 | ||||