- 密度 [g/cm3]: 0.935
- 拉伸強(qiáng)度 [MPa]: 16.9993
- 彎曲模量 [MPa]: 0.4200
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | ASTM D1505 |
| Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | ASTM D2240 |
| Tensile Strength, Yield | 16.9993 MPa | 2465.54 psi | 2"/min; ASTM D638 |
| Elongation at Break | 520 % | 520 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.4200 GPa | 60.91 ksi | ASTM D790 |
| Impact | 17 @Temperature -20.0 °C | 17 @Temperature -4.00 °F | J/mm, instrumented impact, rotomolded test sample; ICO R&D1.14 |