- 密度 [g/cm3]: 0.937
- 拉伸強度 [MPa]: 19.0
- 彎曲模量 [MPa]: 0.780
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1500 hour @Temperature 50.0 °C | >= 1500 hour @Temperature 122 °F | Condition B; ASTM D 1693 |
| High Load Melt Index | 21 g/10 min @Load 21.6 kg, Temperature 190 °C | 21 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 Type IV |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 Type IV |
| Flexural Modulus | 0.780 GPa | 113 ksi | ASTM D790 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 210 °C | 379 - 410 °F | stock temperature |