- 密度 [g/cm3]: 0.955
- 拉伸強度 [MPa]: 27.6
- 彎曲模量 [MPa]: 1.34
- 脆化溫度 [℃]: -83.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition A (100% Igepal), F50; ASTM D1693 |
| >= 1000 hour | >= 1000 hour | Condition B (10% Igepal), F50; ASTM D1693 | |
| High Load Melt Index | 5.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 5.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2" (50mm) per min.; ASTM D638 Type IV |
| Elongation at Break | >= 600 % | >= 600 % | 2" (50mm) per min.; ASTM D638 Type IV |
| Flexural Modulus | 1.34 GPa | 195 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -83.9 °C | <= -119 °F | ASTM D746 |