- 熔體流動(dòng)速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.962
- 拉伸強(qiáng)度 [MPa]: 31.0
- 彎曲模量 [MPa]: 1.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in3 | ASTM D1505 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ASTM D1895 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| High Load Melt Index | 216 g/10 min @Load 21.6 kg, Temperature 190 °C | 216 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D638 |
| Flexural Modulus | 1.25 GPa | 181 ksi | 3 pt. secant. ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |