- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.939
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | ASTM D1505 |
| Moisture Vapor Transmission | 0.200 cc-mm/m2-24hr-atm | 0.508 cc-mil/100 in2-24hr-atm | ASTM F1249 |
| Melt Flow | 0.20 g/10 min | 0.20 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 420 % | 420 % | ASTM D882 |
| Film Elongation at Break, TD | 630 % | 630 % | ASTM D882 |
| Secant Modulus, MD | 0.520 GPa | 75.4 ksi | ASTM D882 |
| Secant Modulus, TD | 0.660 GPa | 95.7 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.630 g/micron | 16.0 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.4 g/micron | 670 g/mil | ASTM D1922 |
| Dart Drop | 2.70 g/micron | 68.6 g/mil | 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 48.0 MPa | 6960 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 31.0 MPa | 4500 psi | ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 221 °C | 430 °F | |