- 熔體流動速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.96
- 缺口沖擊強度: 1.75
- 拉伸強度 [MPa]: 28.0
- 彎曲模量 [MPa]: 1180
- 熱變形溫度 [℃]: 72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in3 | ASTM-D792 |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | ASTM-D2240 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM-D638 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM-D638 |
| Elongation at Break | 2036 % | 2036 % | ASTM-D638 |
| Elongation at Yield | 11 % | 11 % | ASTM-D638 |
| Flexural Modulus, 1% Secant | 1180 MPa | 171000 psi | ASTM-D790 |
| Izod Impact, Notched | 1.75 J/cm | 3.28 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM-D648 |
| Vicat Softening Point | 127 °C @Load 1.02 kg | 261 °F @Load 2.25 lb | ASTM-D1525 |