- 熔體流動(dòng)速率 [g/10min]: 1.7
- 密度 [g/cm3]: 0.944
- 拉伸強(qiáng)度 [MPa]: 31.0
- 彎曲模量 [MPa]: 0.850
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in3 | ISO 1183/ISO 1872-2 | ||
| Environmental Stress Crack Resistance | >= 5.0 hour @Temperature 50.0 °C | >= 5.0 hour @Temperature 122 °F | Igepal 10%;F0; IEC 60811-4-1/B | ||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.7 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 58 | 58 | 3s; ISO 868 | ||
| 61 | 61 | 1s; ISO 868 | |||
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | 900 % | 900 % | 50mm/min; ISO 527 | ||
| Flexural Modulus | 0.850 GPa | 123 ksi | ASTM D790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | DC; IEC 60093 | ||
| Dielectric Strength | 70.0 kV/mm | 1780 kV/in | IEC 60243 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 90.0 °C | 194 °F | preheating temperature | ||
| Melt Temperature | 180 - 190 °C | 356 - 374 °F | |||
| Die Cooling Temperature | 60.0 °C | 140 °F | cooling water | ||
| Descriptive Properties | |||||
| High Temperature Pressure Test, % | < 10% | 115°C; 6 hours; IEC 60811-3-1 | |||