- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.94
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.267
- 拉伸強度 [MPa]: 27.6
- 斷裂伸長率 [%]: 17.2
- 彎曲強度 [MPa]: 11.0
- 彎曲模量 [MPa]: 0.965
- 硬度: 50.0
- 熱變形溫度 [℃]: 72.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 - 1.53 g/cc | 0.0340 - 0.0553 lb/in3 | Average value: 1.16 g/cc Grade Count:55 |
| Filler Content | 10.0 - 50.0 % | 10.0 - 50.0 % | Average value: 25.7 % Grade Count:14 |
| Water Absorption | 0.0100 - 0.300 % | 0.0100 - 0.300 % | Average value: 0.0786 % Grade Count:36 |
| Linear Mold Shrinkage | 0.00100 - 0.0300 cm/cm | 0.00100 - 0.0300 in/in | Average value: 0.00587 cm/cm Grade Count:47 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.0350 cm/cm | 0.00300 - 0.0350 in/in | Average value: 0.0107 cm/cm Grade Count:14 |
| Linear Mold Shrinkage, Transverse | 0.00800 - 0.00900 cm/cm | 0.00800 - 0.00900 in/in | Average value: 0.00833 cm/cm Grade Count:3 |
| Melt Flow | 0.200 - 10.0 g/10 min | 0.200 - 10.0 g/10 min | Average value: 3.74 g/10 min Grade Count:13 |
| Ash | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 24.0 % Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 50.0 - 112 | 50.0 - 112 | Average value: 74.3 Grade Count:36 |
| Tensile Strength, Ultimate | 11.0 - 113 MPa | 1600 - 16400 psi | Average value: 45.5 MPa Grade Count:31 |
| 9.00 - 161.337 MPa @Temperature -40.0 - 120 °C | 1310 - 23400.0 psi @Temperature -40.0 - 248 °F | Average value: 55.1 MPa Grade Count:2 | |
| Tensile Strength, Yield | 27.6 - 60.7 MPa | 4000 - 8800 psi | Average value: 45.3 MPa Grade Count:28 |
| Elongation at Break | 1.00 - 290 % | 1.00 - 290 % | Average value: 14.7 % Grade Count:48 |
| Elongation at Yield | 2.00 - 3.00 % | 2.00 - 3.00 % | Average value: 2.75 % Grade Count:4 |
| Modulus of Elasticity | 0.700 - 13.6 GPa | 102 - 1970 ksi | Average value: 4.59 GPa Grade Count:29 |
| 7.17055 - 15.2374 GPa @Temperature -40.0 - 93.3 °C | 1040.02 - 2210.03 ksi @Temperature -40.0 - 200 °F | Average value: 11.2 GPa Grade Count:1 | |
| Flexural Yield Strength | 17.2 - 186 MPa | 2500 - 27000 psi | Average value: 68.8 MPa Grade Count:48 |
| 61.3633 - 215.116 MPa @Temperature -40.0 - 93.3 °C | 8900.02 - 31200.1 psi @Temperature -40.0 - 200 °F | Average value: 138 MPa Grade Count:1 | |
| Flexural Modulus | 0.965 - 11.7 GPa | 140 - 1700 ksi | Average value: 3.89 GPa Grade Count:54 |
| 1.40 - 14.0653 GPa @Temperature -40.0 - 120 °C | 203 - 2040.03 ksi @Temperature -40.0 - 248 °F | Average value: 5.42 GPa Grade Count:2 | |
| Compressive Yield Strength | 9.50 - 55.2 MPa | 1380 - 8000 psi | Average value: 26.8 MPa Grade Count:7 |
| Izod Impact, Notched | 0.267 - 3.74 J/cm | 0.500 - 7.00 ft-lb/in | Average value: 1.08 J/cm Grade Count:53 |
| 2.1356 - 4.59154 J/cm @Temperature -40.0 - 93.3 °C | 4.0009 - 8.60184 ft-lb/in @Temperature -40.0 - 200 °F | Average value: 3.36 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 1.17 - 13.3 J/cm | 2.20 - 25.0 ft-lb/in | Average value: 5.86 J/cm Grade Count:31 |
| Charpy Impact Unnotched | 1.70 - 2.00 J/cm2 | 8.09 - 9.52 ft-lb/in2 | Average value: 1.83 J/cm2 Grade Count:3 |
| Charpy Impact, Notched | 2.40 - 10.0 J/cm2 | 11.4 - 47.6 ft-lb/in2 | Average value: 5.13 J/cm2 Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+16 ohm-cm | 1000 - 1.00e+16 ohm-cm | Average value: 6.64e+15 ohm-cm Grade Count:22 |
| Surface Resistance | 100000 - 1.00e+13 ohm | 100000 - 1.00e+13 ohm | Average value: 2.50e+12 ohm Grade Count:3 |
| Dielectric Constant | 2.30 - 2.80 | 2.30 - 2.80 | Average value: 2.65 Grade Count:6 |
| Dielectric Strength | 11.8 - 45.0 kV/mm | 300 - 1140 kV/in | Average value: 19.3 kV/mm Grade Count:15 |
| Dissipation Factor | 0.00400 - 0.00800 | 0.00400 - 0.00800 | Average value: 0.00667 Grade Count:6 |
| Arc Resistance | 140 - 180 sec | 140 - 180 sec | Average value: 147 sec Grade Count:6 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.8 - 170 μm/m-°C | 11.0 - 94.4 μin/in-°F | Average value: 65.2 μm/m-°C Grade Count:27 |
| Thermal Conductivity | 0.288 - 0.400 W/m-K | 2.00 - 2.78 BTU-in/hr-ft2-°F | Average value: 0.336 W/m-K Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 - 143 °C | 162 - 290 °F | Average value: 123 °C Grade Count:42 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.7 - 127 °C | 125 - 260 °F | Average value: 110 °C Grade Count:45 |
| Vicat Softening Point | 85.0 - 92.0 °C | 185 - 198 °F | Average value: 88.3 °C Grade Count:3 |
| Flammability, UL94 | HB | HB | Grade Count:34 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 40.0 - 227 °C | 104 - 440 °F | Average value: 188 °C Grade Count:22 |
| Melt Temperature | 191 - 249 °C | 375 - 480 °F | Average value: 222 °C Grade Count:7 |
| Mold Temperature | 21.1 - 65.6 °C | 70.0 - 150 °F | Average value: 44.1 °C Grade Count:25 |
| Drying Temperature | 79.4 - 100 °C | 175 - 212 °F | Average value: 84.9 °C Grade Count:6 |
| Dry Time | 2.00 - 3.00 hour | 2.00 - 3.00 hour | Average value: 2.30 hour Grade Count:5 |
| Injection Pressure | 4.96 - 124 MPa | 720 - 18000 psi | Average value: 80.4 MPa Grade Count:22 |