- 熔體流動速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.87
- 拉伸強度 [MPa]: 18.0
- 彎曲強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.689
- 脆化溫度 [℃]: -90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.870 - 1.47 g/cc | 0.0314 - 0.0531 lb/in3 | Average value: 0.959 g/cc Grade Count:25 |
| Volatiles | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:7 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 - 50.0 °C | >= 1000 hour @Temperature 122 - 122 °F | Average value: 1000 hour Grade Count:3 |
| Melt Flow | 0.350 - 6.10 g/10 min | 0.350 - 6.10 g/10 min | Average value: 1.69 g/10 min Grade Count:21 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 17.0 - 26.5 MPa | 2470 - 3840 psi | Average value: 21.0 MPa Grade Count:17 |
| Tensile Strength, Yield | 18.0 - 26.0 MPa | 2610 - 3770 psi | Average value: 20.1 MPa Grade Count:5 |
| 6.00 - 47.0 MPa @Temperature -40.0 - 100 °C | 870 - 6820 psi @Temperature -40.0 - 212 °F | Average value: 26.5 MPa Grade Count:1 | |
| Elongation at Break | 230 - 540 % | 230 - 540 % | Average value: 367 % Grade Count:22 |
| 110 - 170 % @Temperature -40.0 - 100 °C | 110 - 170 % @Temperature -40.0 - 212 °F | Average value: 140 % Grade Count:1 | |
| Elongation at Yield | 7.00 - 16.0 % @Temperature -40.0 - 100 °C | 7.00 - 16.0 % @Temperature -40.0 - 212 °F | Average value: 11.5 % Grade Count:1 |
| Modulus of Elasticity | 0.00600 - 1.30 GPa | 0.870 - 189 ksi | Average value: 0.639 GPa Grade Count:9 |
| 0.130 - 3.30 GPa @Temperature -40.0 - 100 °C | 18.9 - 479 ksi @Temperature -40.0 - 212 °F | Average value: 1.72 GPa Grade Count:1 | |
| Flexural Modulus | 0.689 - 1.20 GPa | 100 - 174 ksi | Average value: 0.792 GPa Grade Count:5 |
| 0.167 - 2.60 GPa @Temperature -40.0 - 100 °C | 24.2 - 377 ksi @Temperature -40.0 - 212 °F | Average value: 1.38 GPa Grade Count:1 | |
| Charpy Impact, Notched | 999.9 - 999.9 J/cm2 @Temperature 100 - 100 °C | 4759 - 4759 ft-lb/in2 @Temperature 212 - 212 °F | Grade Count:1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 4.10e+15 ohm-cm | 4.10e+15 ohm-cm | Average value: 4.10e+15 ohm-cm Grade Count:3 |
| 1.40e+15 - 2.70e+15 ohm-cm @Temperature 90.0 - 90.0 °C | 1.40e+15 - 2.70e+15 ohm-cm @Temperature 194 - 194 °F | Average value: 2.27e+15 ohm-cm Grade Count:3 | |
| Insulation Resistivity | 15000 Megaohm/1000 m | 49200 Megaohm/1000 ft | Average value: 15000 Megaohm/1000 m Grade Count:3 |
| 5000 - 10000 Megaohm/1000 m @Temperature 90.0 - 90.0 °C | 16400 - 32800 Megaohm/1000 ft @Temperature 194 - 194 °F | Average value: 8330 Megaohm/1000 m Grade Count:3 | |
| Dielectric Constant | 2.30 - 2.40 | 2.30 - 2.40 | Average value: 2.33 Grade Count:3 |
| Dielectric Strength | 1.26 - 1.38 kV/mm | 32.0 - 35.0 kV/in | Average value: 1.33 kV/mm Grade Count:3 |
| Dissipation Factor | 0.000500 - 0.000600 | 0.000500 - 0.000600 | Average value: 0.000567 Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 140 - 190 μm/m-°C | 77.8 - 106 μin/in-°F | Average value: 164 μm/m-°C Grade Count:7 |
| 100 - 100 μm/m-°C @Temperature -90.0 - -30.0 °C | 55.6 - 55.6 μin/in-°F @Temperature -130 - -22.0 °F | Average value: 100 μm/m-°C Grade Count:1 | |
| Specific Heat Capacity | 1.80 - 2.03 J/g-°C | 0.430 - 0.485 BTU/lb-°F | Average value: 1.91 J/g-°C Grade Count:7 |
| Thermal Conductivity | 0.450 - 0.490 W/m-K | 3.12 - 3.40 BTU-in/hr-ft2-°F | Average value: 0.468 W/m-K Grade Count:8 |
| Vicat Softening Point | 50.0 - 129 °C | 122 - 264 °F | Average value: 113 °C Grade Count:12 |
| Brittleness Temperature | -90.0 °C | -130 °F | Average value: -90.0 °C Grade Count:3 |
| Shrinkage | <= 4.00 % @Temperature 130 - 130 °C | <= 4.00 % @Temperature 266 - 266 °F | Average value: 4.00 % Grade Count:1 |
| <= 4.00 % @Time 3600 - 3600 sec | <= 4.00 % @Time 1.00 - 1.00 hour | Average value: 4.00 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 326 °C | 338 - 619 °F | Average value: 233 °C Grade Count:6 |
| Die Temperature | 180 - 230 °C | 356 - 446 °F | Average value: 206 °C Grade Count:20 |
| Melt Temperature | 140 - 200 °C | 284 - 392 °F | Average value: 173 °C Grade Count:20 |
| Head Temperature | 170 - 210 °C | 338 - 410 °F | Average value: 199 °C Grade Count:19 |
| Screw Cooling Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Average value: 80.0 °C Grade Count:7 |