- 熔體流動(dòng)速率 [g/10min]: 50.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ISO 1183 | ||
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.015 - 0.030 cm/cm | 0.015 - 0.030 in/in | |||
| Melt Flow | >= 50 g/10 min @Load 2.16 kg, Temperature 190 °C | >= 50 g/10 min @Load 4.76 lb, Temperature 374 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 9.00 MPa | 1310 psi | |||
| Elongation at Yield | 20 % | 20 % | |||
| Modulus of Elasticity | 0.300 GPa | 43.5 ksi | |||
| Charpy Impact Unnotched | NB | NB | flatwise; ISO 179 1fU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |||
| Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | |||
| 100 °C | 212 °F | short term | |||
| Vicat Softening Point | 80.0 °C | 176 °F | DIN ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 °C | 446 °F | mass temp | ||
| Nozzle Temperature | 190 - 250 °C | 374 - 482 °F | |||
| Zone 1 | 160 - 200 °C | 320 - 392 °F | |||
| Zone 2 | 170 - 220 °C | 338 - 428 °F | |||
| Zone 3 | 180 - 240 °C | 356 - 464 °F | |||
| Mold Temperature | 30.0 - 80.0 °C | 86.0 - 176 °F | |||
| Drying Temperature | 85.0 °C @Time 7200 - 10800 sec | 185 °F @Time 2.00 - 3.00 hour | Dehumidifying dryer | ||
| Descriptive Properties | |||||
| Color | natural color (black) | ||||