- 熔體流動速率 [g/10min]: 4.7
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ISO 1183 |
| Melt Flow | 4.7 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.7 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Stress | 12.0 MPa | 1740 psi | at Yield, TD; ISO 527 |
| 12.0 MPa | 1740 psi | at Yield, MD; ISO 527 | |
| Elongation at Break | 100 % | 100 % | ISO 527, MD |
| 500 % | 500 % | ISO 527, TD | |
| Modulus of Elasticity | 0.250 GPa | 36.3 ksi | MD; ISO 527 |
| Tensile Impact | 130 J/cm | 244 ft-lb/in | ASTM D4272 |
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 |
| Tear Strength | 30.0 kN/m | 171 pli | TD; ISO 6383-2 |
| 90.0 kN/m | 514 pli | MD; ISO 6383-2 | |
| Optical Properties | Metric | English | Comments |
| Haze | 12.5 % | 12.5 % | ASTM D1003A |
| Gloss | 50 % | 50 % | ASTM D2457 |