- 熔體流動速率 [g/10min]: 4.7
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ISO 1183 | ||
| Melt Flow | 4.7 g/10 min | 4.7 g/10 min | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 13.0 MPa | 1890 psi | at Yield, TD; ISO R527-1 | ||
| 13.0 MPa | 1890 psi | at Yield, MD; ISO R527-1 | |||
| Film Elongation at Break, MD | 100 % | 100 % | ISO R527-1 | ||
| Film Elongation at Break, TD | >= 450 % | >= 450 % | ISO R527-1 | ||
| Modulus of Elasticity | 0.230 GPa | 33.4 ksi | MD; ISO R527-1 | ||
| 0.250 GPa | 36.3 ksi | TD; ISO R527-1 | |||
| Tensile Impact | 130 J/cm | 244 ft-lb/in | ASTM D4272 | ||
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 | ||
| Tear Strength | 30.0 kN/m | 171 pli | TD; ISO 6383-2 | ||
| 90.0 kN/m | 514 pli | MD; ISO 6383-2 | |||
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ISO R527-1 | ||
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ISO R527-1 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12 % | 12 % | ASTM D1003A | ||
| Gloss | 50 % | 50 % | ASTM D2457 | ||
| Descriptive Properties | |||||
| Clarity, mV | 28 | Sabtec | |||