- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.916
- 拉伸強度 [MPa]: 9.03
- 彎曲強度 [MPa]: 8.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in3 | ASTM D1505 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | ASTM D638 |
| Tensile Strength, Yield | 9.03 MPa | 1310 psi | ASTM D638 |
| Elongation at Break | 430 % | 430 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 83.9 °C | 183 °F | ASTM D1525 |