- 熔體流動速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.92
- 拉伸強度 [MPa]: 9.0
- 彎曲強度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 450 % | 450 % | ASTM D882 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Modulus of Elasticity | 0.221 GPa | 32.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.166 GPa | 24.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.173 GPa | 25.1 ksi | ASTM D882 |
| Dart Drop | 3.15 g/micron | 80.0 g/mil | ASTM D1709 |
| Dart drop Test | 80.0 g | 0.176 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Gloss | 63 % | 63 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 - 171 °C | 320 - 340 °F | |