- 熔體流動速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ExxonMobil Method |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Antiblock Level | 4000 ppm | 4000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1500 psi | ASTM D882 |
| Film Elongation at Break, MD | 130 % | 130 % | ASTM D882 |
| Film Elongation at Break, TD | 570 % | 570 % | ASTM D882 |
| Elmendorf Tear Strength MD | 280 g | 280 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 120 g | 120 g | ASTM D1922 |
| Dart drop Test | 190 g | 0.419 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.1 MPa | 3500 psi | ASTM D882 |
| 1% Secant Modulus, MD | 186 MPa | 27000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 241 MPa | 35000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 109 °C | 229 °F | Peak Melting Temperature; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
| Haze | 20 % | 20 % | ASTM D1003 |
| Gloss | 33 % | 33 % | 45°; ASTM D2457 |