- 熔體流動速率 [g/10min]: 2.1
- 密度 [g/cm3]: 0.9185
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9185 g/cc | 0.03318 lb/in3 | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 |
| Secant Modulus, MD | 0.150 GPa | 21.8 ksi | ASTM D882 |
| Secant Modulus, TD | 0.175 GPa | 25.4 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.60 | >= 0.60 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 5.90 g/micron | 150 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.90 g/micron | 99.1 g/mil | ASTM D1922 |
| Dart Drop | 2.40 g/micron | 61.0 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 18.0 MPa | 2610 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % @Thickness 0.0250 mm | 12 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 40 % | 40 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 190 °C | 338 - 374 °F | |