- 熔體流動速率 [g/10min]: 1.7
- 密度 [g/cm3]: 0.918
- 拉伸強度 [MPa]: 10.0
- 彎曲強度 [MPa]: 12.0
- 彎曲模量 [MPa]: 0.200
- 脆化溫度 [℃]: -73.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D4883 | ||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.7 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | 500 mm/min (20 in./min.); Type IV Specimen; ASTM D638 | ||
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | 500 mm/min (20 in./min.); Type IV Specimen; ASTM D638 | ||
| Elongation at Break | 500 % | 500 % | 500 mm/min (20 in./min.); Type IV Specimen; ASTM D638 | ||
| Flexural Modulus | 0.200 GPa | 29.0 ksi | 2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -73.0 °C | <= -99.4 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Process | Injection Molding | ||||
| region | US & Canada | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.