- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg | 0.70 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.3 MPa | 1490 psi | |
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1490 psi | |
| Film Elongation at Break, MD | 360 % | 360 % | |
| Film Elongation at Break, TD | 530 % | 530 % | |
| Coefficient of Friction | 0.70 | 0.70 | |
| Elmendorf Tear Strength MD | 270 g | 270 g | |
| Elmendorf Tear Strength TD | 290 g | 290 g | |
| Elmendorf Tear Strength, MD | 6.80 g/micron | 173 g/mil | |
| Elmendorf Tear Strength, TD | 7.30 g/micron | 185 g/mil | |
| Dart Drop | 3.50 g/micron | 88.9 g/mil | |
| Film Tensile Strength at Break, MD | 27.6 MPa | 4000 psi | |
| Film Tensile Strength at Break, TD | 19.3 MPa | 2800 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 8.5 % | 8.5 % | |
| Gloss | 64 % | 64 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 218 °C | 424 °F | Film extrusion temperature |