- 熔體流動(dòng)速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.922
- 拉伸強(qiáng)度 [MPa]: 10.17
- 彎曲模量 [MPa]: 212
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | ASTM D-1505 | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 45 | 45 | |||
| Tensile Strength, Yield | 10.17 MPa | 1475 psi | ASTM D-638 | ||
| Elongation at Break | 700 % | 700 % | >700; ASTM D-638 | ||
| Flexural Modulus, 1% Secant | 212 MPa | 30700 psi | ASTM D-790 | ||
| Descriptive Properties | |||||
| process | Extrusion | ||||
| region | Europe/Turkey | ||||