- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.01
- 缺口沖擊強度: 0.52
- 拉伸強度 [MPa]: 16.0
- 彎曲強度 [MPa]: 11.0
- 熱變形溫度 [℃]: 51.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in3 | |||
| Linear Mold Shrinkage | 0.014 - 0.016 cm/cm | 0.014 - 0.016 in/in | ISO 294-4 | ||
| Melt Flow | 1.0 g/10 min @Load 10.0 kg, Temperature 190 °C | 1.0 g/10 min @Load 22.0 lb, Temperature 374 °F | ISO 1133 | ||
| High Load Melt Index | 4.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 4.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 57 | 57 | ISO 868 | ||
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | ISO 527 | ||
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ISO 527 | ||
| Elongation at Break | 600 % | 600 % | ISO 527 | ||
| Elongation at Yield | 50 % | 50 % | ISO 527 | ||
| Modulus of Elasticity | 0.400 GPa | 58.0 ksi | ISO 178 | ||
| Izod Impact, Notched | 0.520 J/cm @Thickness 4.00 mm, Temperature -20.0 °C | 0.974 ft-lb/in @Thickness 0.157 in, Temperature -4.00 °F | ISO 180 | ||
| NB @Thickness 4.00 mm, Temperature 23.0 °C | NB @Thickness 0.157 in, Temperature 73.4 °F | ISO 180 | |||
| Izod Impact, Unnotched | 1.25 J/cm @Thickness 4.00 mm, Temperature -20.0 °C | 2.34 ft-lb/in @Thickness 0.157 in, Temperature -4.00 °F | ISO 180 | ||
| NB @Thickness 4.00 mm, Temperature 23.0 °C | NB @Thickness 0.157 in, Temperature 73.4 °F | ISO 180 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 1000 ohm-cm | <= 1000 ohm-cm | ISO D-257 | ||
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | ISO D-257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ISO 75/Method Bf | ||
| Vicat Softening Point | 100 °C | 212 °F | Rate A; ISO 306/A50 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |||
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Dry Time | 3 hour | 3 hour | At 90°C; If stored for longer than 1 year | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | When Produced | ||
| Injection Pressure | 60.0 - 80.0 MPa | 8700 - 11600 psi | |||
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions | ||
| Descriptive Properties | |||||
| Appearance | Granule | ||||
| Color | Black | ||||
| Injection Speed | Moderate | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.