- 熔體流動速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ASTM D 792 | ||
| Thickness | 20.0 microns | 0.787 mil | |||
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D 882 | ||
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D 882 | ||
| Film Elongation at Break, MD | 498 % | 498 % | ASTM D 882 | ||
| Film Elongation at Break, TD | 775 % | 775 % | ASTM D 882 | ||
| Elmendorf Tear Strength MD | 63 g | 63 g | ASTM D 1922 | ||
| Elmendorf Tear Strength TD | 350 g | 350 g | ASTM D 1922 | ||
| Elmendorf Tear Strength, MD | 3.15 g/micron | 80.0 g/mil | ASTM D 1922 | ||
| Elmendorf Tear Strength, TD | 17.5 g/micron | 445 g/mil | ASTM D 1922 | ||
| Film Tensile Strength at Break, MD | 36.0 MPa | 5220 psi | ASTM D 882 | ||
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D 882 | ||
| 1% Secant Modulus, MD | 156 MPa | 22600 psi | ASTM D 882 | ||
| 1% Secant Modulus, TD | 177 MPa | 25700 psi | ASTM D 882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.3 % | 1.3 % | ASTM D 1003 | ||
| Gloss | 91 % | 91 % | 45°; ASTM D 2457 | ||
| Descriptive Properties | |||||
| Low Friction Puncture | 9 (ft-lb/mil) | NOVA Chemicals test method | |||