- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D1505 | ||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 440 % | 440 % | ASTM D882 | ||
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 | ||
| Secant Modulus, MD | 0.255 GPa | 37.0 ksi | 1% Strain; ASTM D882 | ||
| Secant Modulus, TD | 0.317 GPa | 46.0 ksi | 1% Strain; ASTM D882 | ||
| Coefficient of Friction | 0.13 | 0.13 | ASTM D1894 | ||
| Elmendorf Tear Strength MD | 400 g | 400 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 910 g | 910 g | ASTM D1922 | ||
| Dart drop Test | 130 g | 0.287 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 29.6 MPa | 4300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 182 - 221 °C | 360 - 430 °F | |||
| Blow-up Ratio (BUR) | 1.5 - 2.5 | 1.5 - 2.5 | |||
| Descriptive Properties | |||||
| Antiblock | Various | ||||
| Form | Pellets | ||||
| Slip | Various | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.