- 熔體流動速率 [g/10min]: 2.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.914 - 0.916 g/cc | 0.914 - 0.916 g/cc | ASTM D1505 |
| Melt Flow | 2.2 - 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.2 - 2.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 480 % | 480 % | Ultimate; ASTM D882 |
| Film Elongation at Break, TD | 750 % | 750 % | Ultimate; ASTM D882 |
| Elmendorf Tear Strength MD | 24 g | 24 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 30 g | 30 g | ASTM D1922 |
| Dart drop Test | 340 g | 0.750 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.2 MPa | 5830 psi | Ultimate; ASTM D882 |
| Film Tensile Strength at Break, TD | 34.3 MPa | 4970 psi | Ultimate; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.70 % | 0.70 % | ASTM D1003 |
| Gloss | 155 % | 155 % | 45°; ASTM D2457 |