- 熔體流動速率 [g/10min]: 0.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.918 - 0.922 g/cc | 0.918 - 0.922 g/cc | ASTM D1505 |
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 37.3 MPa | 5410 psi | 50 mm/min; ASTM D638 |
| Film Elongation at Break, MD | 670 % | 670 % | Ultimate; ASTM D882 |
| Film Elongation at Break, TD | 770 % | 770 % | Ultimate; ASTM D882 |
| Elongation at Break | 850 % | 850 % | 50mm/min, Ultimate; ASTM D638 |
| Elmendorf Tear Strength MD | 15.5 g | 15.5 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 26.4 g | 26.4 g | ASTM D1922 |
| Dart drop Test | 320 g | 0.706 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 51.0 MPa | 7400 psi | Ultimate; ASTM D882 |
| Film Tensile Strength at Break, TD | 48.1 MPa | 6980 psi | Ultimate; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 103 °C | 217 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.5 % | 9.5 % | ASTM D1003 |
| Gloss | 97 % | 97 % | 45°; ASTM D2457 |