- 熔體流動速率 [g/10min]: 0.59
- 密度 [g/cm3]: 0.93
- 拉伸強度 [MPa]: 11.0
- 彎曲模量 [MPa]: 0.365
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition A - 10% Igepal?; ASTM D1693 |
| Absorption Coefficient | 440 | 440 | ASTM D3349 |
| Carbon Black Loading | 2.6 % | 2.6 % | |
| Melt Flow | 0.59 g/10 min | 0.59 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57 | 57 | ASTM D224 |
| Tensile Strength at Break | 16.5 MPa | 2400 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 650 % | 650 % | ASTM D638 |
| Flexural Modulus | 0.365 GPa | 53.0 ksi | 1% Secant; ASTM D790 |
| 1% Secant Modulus | 248 MPa | 36000 psi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.5 @Frequency 1e+6 Hz | 2.5 @Frequency 1e+6 Hz | ASTM D1531 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Dissipation Factor | 0.00040 @Frequency 1e+6 Hz | 0.00040 @Frequency 1e+6 Hz | ASTM D1531 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 200 μm/m-°C @Temperature 20.0 °C | 111 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 154 - 163 °C | 310 - 325 °F | |
| Zone 2 | 177 - 193 °C | 350 - 380 °F | |
| Zone 3 | 193 - 210 °C | 380 - 410 °F | |
| Zone 4-x | 204 - 218 °C | 400 - 425 °F | |
| Adapter Temperature | 204 - 218 °C | 400 - 425 °F | |
| Die Temperature | 204 - 218 °C | 400 - 425 °F | |