- 密度 [g/cm3]: 1.68
- 吸水率 [%]: 0.05
- 缺口沖擊強度: 1.22
- 彎曲模量 [MPa]: 12.5
- 熱變形溫度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in3 | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | MD |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 153 MPa | 22200 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 215 MPa | 31200 psi | ASTM D790 |
| Flexural Modulus | 12.5 GPa | 1810 ksi | ASTM D790 |
| Izod Impact, Notched | 1.22 J/cm | 2.29 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm | 635 kV/in @Thickness 0.0787 in | ASTM D149 |
| Arc Resistance | 135 sec | 135 sec | Tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 175 - 249 V | 175 - 249 V | IEC Pub1.112, class 3; IEC Method |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 μm/m-°C @Temperature 20.0 °C | 11.1 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | By DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Thermal index; ASTM UL746B |
| 225 °C | 437 °F | Ball pressure temperature; IEC Method | |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 255 - 270 °C | 491 - 518 °F | |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | |