- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 1.3
- 斷裂伸長率 [%]: 196
- 彎曲強度 [MPa]: 123.0
- 彎曲模量 [MPa]: 9.30
- 熱變形溫度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in3 | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength, Ultimate | 123 MPa | 17800 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Flexural Modulus | 9.30 GPa | 1350 ksi | ASTM D790 |
| Compressive Yield Strength | 108 MPa | 15700 psi | ASTM D695 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 36 | 36 | ASTM D1044 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm | 584 kV/in @Thickness 0.0787 in | ASTM D149 |
| Arc Resistance | 85 sec | 85 sec | ASTM D495 |
| Comparative Tracking Index | 220 V | 220 V | IEC test |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| UL RTI, Electrical | 130 °C | 266 °F | UL-746B |
| Flammability, UL94 | V-0 @Thickness 0.907 mm | V-0 @Thickness 0.0357 in | UL-94 |