- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.05
- 缺口沖擊強(qiáng)度: 1.8
- 斷裂伸長(zhǎng)率 [%]: 216
- 彎曲強(qiáng)度 [MPa]: 147.0
- 彎曲模量 [MPa]: 9.10
- 熱變形溫度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in3 | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength, Ultimate | 147 MPa | 21300 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ASTM D790 |
| Compressive Yield Strength | 108 MPa | 15700 psi | ASTM D695 |
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 15 | 15 | ASTM D1044 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm | 635 kV/in @Thickness 0.0787 in | ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | 255 V | 255 V | IEC test |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| UL RTI, Electrical | 130 °C | 266 °F | UL-746B |
| Flammability, UL94 | HB @Thickness 0.7937 mm | HB @Thickness 0.03125 in | |