- 吸水率 [%]: 0.03
- 缺口沖擊強度: 0.8
- 彎曲模量 [MPa]: 7.58
- 硬度: 119.0
- 熱變形溫度 [℃]: 212.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | ASTM D792 | ||
| Water Absorption | 0.030 % @Time 86400 sec | 0.030 % @Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 1.50 - 3.20 mm | 0.0030 - 0.0050 in/in @Thickness 0.0591 - 0.126 in | SABIC Method | ||
| 0.0050 - 0.0080 cm/cm @Thickness 3.20 - 4.60 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 - 0.181 in | SABIC Method | |||
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in | SABIC Method | ||
| 0.0060 - 0.0090 cm/cm @Thickness 3.20 - 4.60 mm | 0.0060 - 0.0090 in/in @Thickness 0.126 - 0.181 in | SABIC Method | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM D785 | ||
| Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 | ||
| Flexural Strength | 179 MPa | 26000 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Flexural Modulus | 7.58 GPa | 1100 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D4812 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.80e+16 ohm-cm | 1.80e+16 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.8 @Frequency 100 Hz | 3.8 @Frequency 100 Hz | ASTM D150 | |||
| Dielectric Strength | 18.8 kV/mm @Thickness 3.20 mm | 478 kV/in @Thickness 0.126 in | in air; ASTM D149 | ||
| 23.2 kV/mm @Thickness 1.60 mm | 589 kV/in @Thickness 0.0630 in | in oil; ASTM D149 | |||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | ASTM D150 | ||
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 | ||
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A | ||
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 21.6 μm/m-°C @Temperature -40.0 - 40.0 °C | 12.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | ||
| 21.6 μm/m-°C @Temperature 60.0 - 138 °C | 12.0 μin/in-°F @Temperature 140 - 280 °F | ASTM E 831 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 6.40 mm | 414 °F @Thickness 0.252 in | unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C @Thickness 6.40 mm | 379 °F @Thickness 0.252 in | unannealed; ASTM D648 | ||
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 1.80 mm | V-0 @Thickness 0.0709 in | UL 94 | ||
| 5VA @Thickness 2.99 mm | 5VA @Thickness 0.118 in | UL 94 | |||
| Descriptive Properties | |||||
| Specific Volume | 0.6cm^3/g | ASTM D792 | |||